What is C35000 high leaded brass and what are its main alloying elements?

C35000 is a wrought leaded brass (copper-zinc-lead alloy) with Cu 60.0–63.0%, Zn balance, Pb 0.8–2.0%, and Fe ≤0.15%. The lead phase gives it excellent machinability, which is the main reason to select this grade for screw-machine work.

What ASTM specifications cover C35000 and in what forms is it supplied?

ASTM B135 covers C35000 tube, rod and shapes; it is also supplied as drawn rod and wire. Temper controls the properties — O60 (soft annealed) gives the highest elongation, while H01–H06 cold-worked tempers raise strength and hardness.

What are typical mechanical and physical properties of C35000?

Depending on temper, ultimate tensile strength runs roughly 340–650 MPa, yield 150–420 MPa, and elongation 3–52% (soft tempers at the high end). Electrical conductivity is about 26% IACS and density ~8.5 g/cm³. Machinability rates around 100 (C36000 = 100).

Is C35000 suitable for potable water or RoHS-restricted applications?

No. C35000 contains 0.8–2.0% lead, so it is restricted under RoHS and is not approved for potable-water contact (NSF/ANSI 61). It is used for machined components, fittings, gears, valve parts and other non-water hardware where leaded machinability matters.

Can Linsy Copper supply C35000 to custom sizes with documentation?

Linsy supplies C35000 rod, wire and tube to ASTM with customized diameters, tempers and lengths. Every order ships with an MTR/MTC, SGS reports on request, and RoHS/REACH support. Typical lead time is 10–60 days with low MOQ and a 1-hour quoting response.

C35000 Latão de Alto Teor de Chumbo

Name: C35000 High Leaded Brass
Brand: Linsy Copper

60–63%

Teor de Cobre

0.7–1.2%

Teor de Chumbo

H02/H04/H06

Tempera

O latão C35000 é uma liga de cobre-zinco com chumbo que oferece excelente usinabilidade, aparência atraente e boa resistência à corrosão. É amplamente utilizado em ferragens arquitetônicas, componentes decorativos, peças usinadas de precisão e aplicações de fabricação industrial.

Solicitar Orçamento

Prazo de Entrega: 3-5 Dias Úteis

Visão Geral do Produto

O latão C35000 é uma liga de cobre-zinco de usinagem livre contendo adições controladas de chumbo para melhorar o desempenho de usinagem, mantendo boa resistência e resistência à corrosão. É fabricado conforme ASTM B36, ASTM B134 e normas relacionadas para aplicações que exigem aparência atraente e fabricação eficiente.

Produzido por processos de laminação, trefilação, extrusão e usinagem, o latão C35000 oferece estabilidade dimensional confiável, acabamentos superficiais lisos e boa trabalhabilidade. Sua combinação equilibrada de usinabilidade e apelo estético o torna adequado para aplicações decorativas e funcionais.

O latão C35000 é amplamente utilizado em ferragens arquitetônicas, acabamentos decorativos, conexões elétricas, componentes torneados de precisão e produtos industriais onde aparência e eficiência de usinagem são importantes. É amplamente aplicado nas indústrias de construção, móveis, iluminação, eletrônicos e manufatura.

Principais Características

Boa usinabilidade

Aparência dourada atraente

Boa resistência à corrosão

Adequado para aplicações decorativas

Estabilidade dimensional confiável

Acabamento superficial liso após usinagem

Tamanhos Disponíveis

Forma do Cobre	Espessura (mm)	Largura/Diâmetro (mm)	Comprimento (m)
Barra	-	Φ5-200	1-6
Fio	-	Φ0,05-10	Personalizar
Chapa	0.25-6	500-2500	1-6
Placa	6-200	200-3000	1-6
Tira	0.15-6	8-610	Personalizar
Tubo	DE: φ2-600; PE: φ0,2-100mm	-	1-6
Bobina	0.15-6	3-1250	1-6
Folha	< 0,15	10-1350	Personalizar
Perfil	Personalizado	Personalizar	Personalizar

* Tamanhos personalizados disponíveis mediante solicitação. Entre em contato com nossa equipe de vendas para requisitos especiais.

Especificações Técnicas

Dados de precisão para decisões de engenharia. Todos os valores testados de acordo com as normas ASTM.

01 Propriedades do Material

Especificação	Valor	Notas
Teor de Cu	61-64%	Composição do latão de corte livre
Teor de Pb	1.5-2.5%	Melhora a usinabilidade
Teor de Zn	Restante	Propriedades mecânicas equilibradas
Densidade	8,50 g/cm³	Valor típico
Condutividade Elétrica	~25% IACS	Baseado no temper
Resistência à Tração	320-500 MPa	Depende do temper
Alongamento	≥ 20%	Condição típica recozida/extrudada
Temperas Disponíveis	H01 / H02 / H04 / H06	Tempera personalizável opcional
Fabricação	Usinagem CNC / Torneamento / Rosqueamento	Boa usinabilidade
Norma ASTM	ASTM B36 / ASTM B134	EN e JIS disponíveis

Aplicações e Casos de Uso

Soluções comprovadas em diversos setores. Desde aeroespacial até ambientes marinhos.

Latão Alto Teor de Chumbo C35000 — FAQ

FAQ prático sobre composição do latão com chumbo C35000, especificações ASTM, propriedades e fornecimento para peças usinadas e conexões.

O C35000 é um latão com chumbo forjado (liga de cobre-zinco-chumbo) com Cu 60,0–63,0%, Zn balanceado, Pb 0,8–2,0% e Fe ≤0,15%. A fase de chumbo confere excelente usinabilidade, que é o principal motivo para selecionar este grau para trabalhos em máquinas de parafusos.

A ASTM B135 cobre tubo, barra e perfis de C35000; também é fornecido como barra trefilada e fio. O temperamento controla as propriedades — O60 (recozido macio) proporciona o maior alongamento, enquanto os temperamentos trabalhados a frio H01–H06 aumentam resistência e dureza.

Dependendo do temperamento, a resistência à tração final varia aproximadamente de 340–650 MPa, limite de escoamento de 150–420 MPa e alongamento de 3–52% (temperamentos macios no extremo superior). A condutividade elétrica é de cerca de 26% IACS e densidade ~8,5 g/cm³. A usinabilidade é avaliada em torno de 100 (C36000 = 100).

Não. O C35000 contém 0,8–2,0% de chumbo, portanto é restrito pela RoHS e não é aprovado para contato com água potável (NSF/ANSI 61). É utilizado em componentes usinados, conexões, engrenagens, peças de válvulas e outros hardware não relacionados à água onde a usinabilidade com chumbo é importante.

A Linsy fornece barra, fio e tubo de C35000 conforme ASTM com diâmetros, temperamentos e comprimentos personalizados. Cada pedido é enviado com MTR/MTC, relatórios SGS sob solicitação e suporte RoHS/REACH. O prazo de entrega típico é de 10–60 dias com MOQ baixo e resposta de cotação em 1 hora.