What is C12000 deoxidized low-phosphorus (DLP) copper?

C12000 is phosphorus-deoxidized copper with Cu ≥99.90% and a low phosphorus content of 0.004–0.012%. The small phosphorus removes oxygen, making it weld- and braze-friendly while keeping good conductivity.

What ASTM specifications and forms cover C12000?

ASTM B152 (sheet/strip/plate), B124 (forging rod) and B280 (ACR tube) cover C12000; it is supplied as sheet, strip, rod and tube.

What are typical electrical and mechanical properties?

Conductivity is in the high-80s to mid-90s % IACS (slightly below ETP due to phosphorus), with annealed UTS ~195–250 MPa and elongation ~35–45%. It is not susceptible to hydrogen embrittlement.

How do DLP (C12000) and DHP (C12200) differ — how to choose?

Both are phosphorus-deoxidized. C12000 has the lower phosphorus (0.004–0.012%) and slightly higher conductivity, while C12200 (DHP) has 0.015–0.040% phosphorus and is the standard for plumbing/HVAC tube and brazed assemblies. Choose C12000 when you want a bit more conductivity; choose C12200 for tube and brazing.

Can Linsy Copper supply C12000 with certification?

Linsy supplies C12000 to ASTM with an MTR/MTC, SGS on request, and RoHS/REACH support. Typical lead time is 10–60 days with low MOQ and a 1-hour quoting response.

C12000 Cobre Isento de Oxigênio

Name: C12000 Oxygen-Free Copper
Brand: Linsy Copper

>99,91% Cu

PUREZA

85-90% IACS

CONDUTIVIDADE

H00-H04

TÊMPERA

O Cobre C12000, também conhecido como cobre DLP (Desoxidado com Baixo Fósforo), é um grau de cobre desoxidado com fósforo que oferece boa soldabilidade e condutividade térmica confiável. É comumente usado em trocadores de calor, sistemas de encanamento e aplicações industriais que exigem bom desempenho de fabricação.

Solicitar Orçamento

Prazo de Entrega: 3-5 Dias Úteis

Visão Geral do Produto

O cobre C12000, comumente chamado de cobre DLP, é um grau de cobre desoxidado com baixo fósforo, contendo alta pureza de cobre e teor controlado de fósforo. É fabricado conforme a norma ASTM B152 e normas relacionadas para aplicações que exigem boa condutividade térmica e desempenho de fabricação aprimorado.

Produzido por meio de processos de desoxidação que reduzem o teor de oxigênio residual, o cobre C12000 oferece excelentes características de soldagem e brasagem com risco reduzido de fragilização por hidrogênio. Sua resistência mecânica equilibrada e resistência à corrosão confiável o tornam adequado para diversos sistemas industriais e térmicos.

O cobre C12000 é amplamente utilizado em equipamentos de encanamento, trocadores de calor e sistemas de tubulação industrial onde são necessários desempenho consistente e boa conformabilidade. É comumente aplicado nas indústrias de HVAC, geração de energia e engenharia geral.

Principais Características

Cobre de alta pureza (≥99,91% Cu)

Teor de oxigênio extremamente baixo (≤0,0005%)

Excelente condutividade elétrica (101% IACS)

Condutividade térmica superior

Alta ductilidade e conformabilidade

Adequado para diversos processos de fabricação

Tamanhos Disponíveis

Forma do Cobre	Espessura (mm)	Largura/Diâmetro (mm)	Comprimento (m)
Barra	-	Φ5-200	1-6
Fio	-	Φ0,05-10	Personalizar
Chapa	0.25-6	500-2500	1-6
Placa	6-200	200-3000	1-6
Tira	0.15-6	8-610	Personalizar
Tubo	DE: φ2-600; PE: φ0,2-100mm	-	1-6
Bobina	0.15-6	3-1250	1-6
Folha	< 0,15	10-1350	Personalizar
Perfil	Personalizado	Personalizar	Personalizar

* Tamanhos personalizados disponíveis mediante solicitação. Entre em contato com nossa equipe de vendas para requisitos especiais.

Especificações Técnicas

Dados de precisão para decisões de engenharia. Todos os valores testados de acordo com as normas ASTM.

01 Composição Química

Elemento	Valor (%)
Cu	≥ 99,90
P	0.004–0.012
O	≤ 0,01
Pb	≤ 0,005
Fe	≤ 0,005

02 Propriedades Mecânicas

Propriedade	Condição	Valor
Resistência à Tração	H00	200–260 MPa
Limite de Escoamento	H00	70–120 MPa
Alongamento	H00	≥ 35%
Dureza (HRB)	H00	45–60

03 Propriedades Físicas

Propriedade	Valor
Densidade	8,89 g/cm³
Condutividade Elétrica	85–90% IACS
Condutividade Térmica	340 W/m·K
Ponto de Fusão	1083°C
Expansão Térmica	17,0 ×10⁻⁶ /K

Aplicações e Casos de Uso

Soluções comprovadas em diversos setores. Desde aeroespacial até ambientes marinhos.

Cobre C12000 Deoxidado de Baixo Fósforo (DLP) — FAQ

FAQ prático sobre cobre DLP C12000, especificações ASTM, propriedades e como ele difere do DHP C12200.

O C12000 é cobre deoxidado com fósforo, com Cu ≥99,90% e baixo teor de fósforo de 0,004–0,012%. O pequeno teor de fósforo remove o oxigênio, tornando-o adequado para soldagem e brasagem, mantendo boa condutividade.

ASTM B152 (chapa/tira/lâmina), B124 (barra para forjamento) e B280 (tubo ACR) cobrem o C12000; ele é fornecido como chapa, tira, barra e tubo.

A condutividade fica entre 80 e meados de 90 % IACS (levemente abaixo do ETP devido ao fósforo), com UTS recozido de ~195–250 MPa e alongamento de ~35–45%. Não é suscetível à fragilização por hidrogênio.

Ambos são deoxidados com fósforo. O C12000 tem menor teor de fósforo (0,004–0,012%) e condutividade ligeiramente maior, enquanto o C12200 (DHP) tem 0,015–0,040% de fósforo e é o padrão para tubos de encanamento/HVAC e conjuntos brasados. Escolha C12000 quando precisar de um pouco mais de condutividade; escolha C12200 para tubos e brasagem.

A Linsy fornece C12000 conforme ASTM com MTR/MTC, SGS sob solicitação e suporte RoHS/REACH. O prazo de entrega típico é de 10 a 60 dias, com MOQ baixo e resposta de cotação em 1 hora.