What is C34000 low leaded brass and what is its composition?

C34000 is a wrought leaded brass with Cu 62.0–65.0%, Zn balance, Pb 0.8–1.5%, and Fe ≤0.15%. It balances moderate formability with enough lead for good machinability, sitting between low- and medium-leaded brass families.

What ASTM specifications and forms apply to C34000?

ASTM B135 covers C34000 tube, rod and wire; it is supplied as drawn tube, rod and wire. Common tempers are O60, H01, H02 and H04, selected by the strength and ductility the part needs.

What are typical mechanical and physical properties?

Ultimate tensile strength is roughly 340–650 MPa, yield 103–414 MPa, and elongation up to ~52% in soft temper. Conductivity is about 26% IACS and density ~8.5 g/cm³. Machinability rates around 60–70 (C36000 = 100).

Does C34000 meet RoHS or potable-water requirements?

No. With 0.8–1.5% lead it is outside RoHS limits and is not approved for drinking-water contact. It is used for screw-machine parts, couplings, nuts, rivets and general fittings where leaded machinability is acceptable.

Can Linsy Copper provide C34000 with certification?

Yes. Linsy supplies C34000 to ASTM in custom diameters, tempers and lengths with an MTR/MTC, SGS on request, and RoHS/REACH support. Lead time is typically 10–60 days, with low MOQ and a 1-hour quote response.

C34000 Latão de Baixo Teor de Chumbo

Name: C34000 Low Leaded Brass
Brand: Linsy Copper

60–63%

Teor de Cobre

0.7–1.2%

Teor de Chumbo

H02/H04/H06

Tempera

O latão C34000 é uma liga de cobre-zinco com chumbo que oferece boa usinabilidade, excelente conformabilidade e aparência superficial atraente. É amplamente utilizado em placas de gravação, ferragens decorativas, componentes arquitetônicos e produtos fabricados com precisão.

Solicitar Orçamento

Prazo de Entrega: 3-5 Dias Úteis

Visão Geral do Produto

O latão C34000 é uma liga de cobre-zinco de usinagem livre contendo adições controladas de chumbo para melhorar a usinabilidade, mantendo boa conformabilidade e resistência à corrosão. É fabricado conforme ASTM B36, ASTM B134 e normas relacionadas para aplicações de fabricação decorativa e industrial.

Produzido por processos de laminação, trefilação e conformação de precisão, o latão C34000 oferece características de usinagem suaves, estabilidade dimensional confiável e aparência dourada atraente. Suas propriedades mecânicas equilibradas o tornam adequado para componentes decorativos e funcionais.

O latão C34000 é amplamente utilizado em placas de gravação, acabamentos decorativos, placas de identificação, ferragens arquitetônicas, acessórios elétricos e peças fabricadas industriais onde aparência e usinabilidade são importantes. É amplamente aplicado nas indústrias de construção, sinalização, eletrônicos e manufatura.

Principais Características

Excelente usinabilidade para usinagem CNC e em máquinas de parafuso

Boa estabilidade dimensional

Acabamento superficial liso após usinagem

Boa resistência à corrosão em ambientes gerais

Adequado para produção de alto volume

Resistência mecânica confiável

Tamanhos Disponíveis

Forma do Cobre	Espessura (mm)	Largura/Diâmetro (mm)	Comprimento (m)
Barra	-	Φ5-200	1-6
Fio	-	Φ0,05-10	Personalizar
Chapa	0.25-6	500-2500	1-6
Placa	6-200	200-3000	1-6
Tira	0.15-6	8-610	Personalizar
Tubo	DE: φ2-600; PE: φ0,2-100mm	-	1-6
Bobina	0.15-6	3-1250	1-6
Folha	< 0,15	10-1350	Personalizar
Perfil	Personalizado	Personalizar	Personalizar

* Tamanhos personalizados disponíveis mediante solicitação. Entre em contato com nossa equipe de vendas para requisitos especiais.

Especificações Técnicas

Dados de precisão para decisões de engenharia. Todos os valores testados de acordo com as normas ASTM.

01 Propriedades do Material

Especificação	Valor	Notas
Teor de Cu	60-63%	Composição do latão de corte livre
Teor de Pb	0.7-1.2%	Melhora a usinabilidade
Teor de Zn	Restante	Propriedades mecânicas equilibradas
Densidade	8,48 g/cm³	Valor típico
Condutividade Elétrica	~25% IACS	Baseado no temper
Resistência à Tração	320-500 MPa	Depende do temper
Alongamento	≥ 25%	Condição típica recozida/extrudada
Temperas Disponíveis	H01 / H02 / H04 / H06	Tempera personalizável opcional
Fabricação	Usinagem CNC / Torneamento / Rosqueamento	Boa usinabilidade
Norma ASTM	ASTM B36 / ASTM B134	EN e JIS disponíveis

Aplicações e Casos de Uso

Soluções comprovadas em diversos setores. Desde aeroespacial até ambientes marinhos.

Latão C34000 de Baixo Teor de Chumbo — FAQ

FAQ prático sobre composição do latão com chumbo C34000, especificações ASTM, propriedades e fornecimento para peças de torno automático e conformação.

O C34000 é um latão com chumbo forjado com Cu 62,0–65,0%, Zn balanceado, Pb 0,8–1,5% e Fe ≤0,15%. Ele equilibra conformabilidade moderada com chumbo suficiente para boa usinabilidade, situando-se entre as famílias de latão de baixo e médio teor de chumbo.

A ASTM B135 cobre tubo, barra e fio de C34000; é fornecido como tubo trefilado, barra e fio. Os temperos comuns são O60, H01, H02 e H04, selecionados conforme a resistência e ductilidade necessárias para a peça.

A resistência à tração máxima é de aproximadamente 340–650 MPa, limite de escoamento de 103–414 MPa e alongamento de até ~52% no tempero mole. A condutividade é de cerca de 26% IACS e densidade de ~8,5 g/cm³. A usinabilidade fica em torno de 60–70 (C36000 = 100).

Não. Com 0,8–1,5% de chumbo, está fora dos limites RoHS e não é aprovado para contato com água potável. É utilizado em peças de torno automático, acoplamentos, porcas, rebites e acessórios gerais onde a usinabilidade com chumbo é aceitável.

Sim. A Linsy fornece C34000 conforme ASTM em diâmetros, temperos e comprimentos personalizados, com MTR/MTC, SGS sob solicitação e suporte RoHS/REACH. O prazo de entrega é tipicamente de 10 a 60 dias, com MOQ baixo e resposta de cotação em 1 hora.

Nome *

Empresa

Telefone *

País

Mensagem *

Anexo (Opcional)